The sustained administration of drugs over an extended period of time has significant medical and practical advantages in clinical practice. In recent years, much research has been done in developing systems for the sustained release of biologically active substances, particularly drugs, over periods of time. The purpose of these systems is to dispense the drug or other substance in a controlled manner at a selected physiological site. In the case of drugs used for therapy, presenting the drug in the most efficacious manner to effect treatment is desirable, while simultaneously minimizing complications which may occur as a result, of the drug delivery.

Presently available systems for the sustained release of drugs are generally polymeric composi- tions where the drug or agent is either an integral part of the polymer matrix or layered or contained as a discrete portion of the device. For example, Folkman and Langer in U.S. Patent 4,291,797 describe a delivery device for macromolecules in which the macromolecule is interspersed throughout the polymer matrix.

In U.S. Patent 4,767,628, Hutchinson describes a delivery vehicle formed of polylactide polymer and an acid stable polypeptide interspersed in the matrix. Higuchi in U.S. Patent 3,625,214 describes a sustained release drug delivery device according to a defined release profile by layering the drug and a bioerodible polymer.

Michaels in U.S. Patent 3,867,519 describes a sustained drug delivery device wherein release of the drug is controlled by the composition of an anionic polyvalent metal cation cross-linked polyelectrolyte.

In U.S. Patent 4,093,709 Choi and Heller describe a controlled release device formed from orthoester and orthocarbonate polymers.

While the above systems are useful, they are not appropriate for some applications, such as delivering water-soluble bioactive factors which react with a local cell population at a physiological site. A need exists for systems that can successfully deliver these agents which have favorable release kinetics and allow soluble agents to interact with local cells.

Summary of the Invention

The invention relates to a composition and method for the controlled administration of a bioactive substance to a local cell population in a subject. The composition comprises a bioerodible, surface-eroding polymer having the bioactive

substance interspersed throughout the matrix, which erodes in the biological environment, releasing the bioactive substance to the selected area. The invention also includes a method for delivering water-soluble local-acting substances, particularly proteins, to a specific site in the body of an animal .

The composition and method of the invention allows water-soluble proteins to interact with local cell populations. These proteins are soluble in the physiological environment, and are generally ineffective when introduced i.n_v_iv£ into a biological site because they quickly become diluted and dispersed in the body. The present composition releases soluble proteins directly to a selected site in a concentration sufficient to permit the proteins to interact with the local cell population. The surface-eroding polymers used in the present composition are biocompatible and bioerode in the physiological environment, allowing heterogeneous degradation from the surface of the device, which leads to near zero-order release kinetics. The degradation products of the surface-eroding polymers are non-mutagenic, non-cytotoxic and have a low teratogenic potential.

Pgt_IJ- _. lgd__ escrigtion__ _. pf_the Invention

The present invention provides a system for the controlled or sustained release of bioactive sub¬ stances which interact with local cell populations at a physiological site. The composition is formed

from a bioerodible, surface-eroding polymer and the bioactive substance. The "sustained" or "controlled" release of the substance may be either continuous or discontinuous. The composition of the present invention comprises a bioerodible polymer matrix and a bioactive substance incorporated therein which, when placed in an aqueous physiological environment, releases the bioactive substance in a continuous manner until essentially all of the substance has been released, and the polymer has eroded away. The term "matrix" as used herein denotes a carrier, polymeric phase for the interspersed bioactive substance, which bioerodes in the environment of use, releasing the bioactive substance.

Bioerodible polymers suitable for use in the present invention are polymers which break down or disintegrate over a prolonged period of time when placed in contact with biological fluids. Surface-eroding bioerodible polymers are preferred for use in the present composition. Surface-eroding polymers are, generally, polymers having hydrophobic backbones and hydrolytic linkages, which bioerode from the surface at a constant rate in a biological environment. Surface eroding polymers include polyanhydrides and polyorthoesters .

Polyanhydride polymers are particularly useful for the present compositions. Polyanhydride polymers have several properties which are desirable in a biodegradable, polymeric controlled-release system. These polymers have a hydrophobic backbone

and a water labile linkage, which allows heterogeneous degradation _in vi.v£ from the surface of the polymer, leading to near zero-order release kinetics. The water-labile anhydride linkage provides the basis for the use of a variety of backbones, each having a unique degradation rate. Thus, the rate of degradation in vivo can be con¬ trolled by controlling the length and composition of the polymer backbone. Examples of polyanhydrides which can be used in the present invention include poly[bis (p-carboxyphenoxy) propane anhydride] (PCPP) and poly[bis(p-carboxy) methane anhydride] (PCPM). Co-polymers of polyanhydrides with other substances can also be used. For example, a co-polymer of PCPP and sebacic acid (PCPP-SA) has been shown to be an appropriate material to form a delivery device for soluble proteins. The degradation products of the polyanhydrides are non-mutagenic and non-toxic. In _-lY.£ toxicity studies have shown that polyanhydrides have excellent local system biocompatibility. The characteristics of polyanhydride drug carriers for systemic drugs is described by Leong et al . Leong et al. , J_v_ ip_med__Mat_ _; __Res^, 19:941-955 (1985), Leong et al. J . Biomed^ Mat^ Res^, 0:51-64 (1986). Polyanhydride delivery vehicles of the present invention can be used to deliver highly soluble bioactive factors or substances which regulate local cellular events. These factors are generally characterized in that in vitro they produce a response in a cell population, but do not produce a response when used directly in _yiyo . These

substances or factors must be in the vicinity of the cells which they act upon to be effective. These factors are generally water-soluble polypeptides or proteins, which, when introduced into a physio- logical environment i_n_vi_vo, are soluble in the environment, and so become too diluted to act locally. Bioactive factors having these character¬ istics include factors involved in wound healing or angiogenesis, such as TGF-beta, EGF, FGF and PDGF, which act upon local cell populations.

The term "water" as used herein (e.g. , water- soluble), includes biological fluids, saline and physiologically acceptable buffer.

In one embodiment of the present invention, bioactive factors which promote chondrogenesis and osteogenesis are used. The protein(s) involved in chondrogenesis/osteogenesis interact with the local cells to influence their proliferation and cyto- di ferentiation. Transmembrane experiments have shown that the bioactive factor(s) responsible for the chondro-osteoinduction are soluble in body fluids. Nogami and Urist, , 19:153-163 (1975); Urist et al., Arch. Surg. , 112:612-619 (1977). It has been demonstrated that cold water-soluble proteins from bone matrix extracts will initiate chondrogenesis in in vitro assay systems. Syftes ad and Caplan, Dey_ Biol . ,

104:348-356 (1984); Syftestad et al. , Differentiation, 2£ ^:23 °- ²³⁷ (1985); Lucas et al. , Differentiation, Z ^:47 " ⁵² (1987). However, due to their solubility, these protein fractions do not

induce osteogenesis in_y_Ly£ when implanted alone. It has now been shown that when these proteins are properly formatted in a controlled- elease vehicle, they are capable of inducing cartilage and bone in yi_y£.

Osteogenesis is initiated by an interaction between diffusable bone matrix-derived bioactive factor(s) and local ingrowing cell populations. Reddi and Huggins, P__g _. c _. ___Nat 1..Acad. Sci. USA, _, 59:1601-1605 (1972). These diffusable factors can be extracted from the demineralized matrix. However, these factors are very soluble in physiological solutions and will not initiate osteogenesis when implanted alone into an ectopic site. (Table 1) Demineralized bone matrix may be viewed as a "natural" sustained release vehicle which releases the soluble bioactive factor(s) in an effective manner. The present invention allows the dose and rate of release of bioactive factors exhibited by pieces of demineralized bone matrix to be mimicked.

The chondrp/osteogenic water-soluble proteins used in the present embodiment of the invention are a complex mixture of proteins. Although con- siderable research has been done to isolate the chondro/osteogenic protein from bone matrix, to date no protein has been unequivocally purified to homogeneity. Urist et al. , Prop . Nat' 1. Acad^ Sci_.

USA, 1:371-375 (1984); Seyedin et al. , Proc . Nat'l. , 2:2267-2271 (1985); Sampath et al. ,

Pl££_._N tl1_Acad^._Sci____USA, 84:7109-7113 (1987) ; Sen

et a1. , Dey J_££πιen_t_and_D_i a^e _ f_Car_ti.1ag _and B£ne_Majtri. , pp. 201-219, A. Sen and T. Thornhill (eds.), Alan R. Liss, Inc. , New York (1987); Wang et a1. , Pr£c____Nat___1____Acad___Sci____U_3A, 85:9484-9488 (1988) . Ectopic endochondral ossification occurs through a cascade of events which include recruitment of the local responsive cells, prolifer¬ ation of the cells, and cytodifferentiation. Each of these steps is thought to involve different bioactive factors, i.e. , chemoattractants , mitogens, and chondro/osteogenic factor(s) . Reddi, Current

Ady_. ϊn_£_k_3l ££eι_esis , pp. 77-86, M. Silberman and

H. Slavkin (eds.) , Excerpta Medica, Amsterdam (1982) . A crude mixture of proteins is more likely to contain all the necessary bioactive factors. The water-soluble proteins have been shown to be unable to induce ectopic osteogenesis when implanted alone, but to support the osteogenic cascade when incorpo¬ rated into the herein described composition. When a purified chondro/osteogenic protein becomes available, then the polyanhydride polymers may prove an even more useful delivery vehicle.

The composition of the present invention can be used in manuf cturing controlled-release delivery vehicles, which can be manufactured by recognized methods for preparing controlled-release vehicles. See, U.S. 4,391,727; U.S. 4,767,628. In one embodiment, the present compositions were formed by mixing the selected anhydride polymer and the bioactive factors. Briefly, the polyanhydride polymers or co-polymers were synthesized by

art-recognized techniques. Leong et al . , J_. Bi.£Sj_____.

Mat____Res _^ ___, 1^:941-955 (1985) ; Conix, Macr£____ ;_/ th___ , 2.:95-98 (1966) . The polymers were ground and sieved into a particle size range of from about 90 to about 150 μ . The water-soluble proteins (i.e. , bioactive factors) were mixed with the polymer at the desired ratios, by weight. The relative proportions of polymer to protein will vary depending upon the activity of the protein and the end use of the delivery vehicles. Generally, the protein is present in an amount sufficient, upon release, to interact with the local cell population. The proportion of polymer or co-polymer to protein suitable for the purpose of the present invention will range from about 10% by weight to about 90% by weight of polymer to about 90% to 10% by weight of protein. The preferred amount of protein is from about 20% to about 60% by weight, formulated with sufficient polymer matrix to give 100 parts by weight of the composition.

The mixture of protein and polymer is then molded to form delivery vehicles , which can be shaped in a wide variety of shapes, sizes and forms for delivering the selected bioactive factors to the environemnt of use. For example, the composition can be shaped as buccal and oral devices or articles , vaginal and intrauterine devices or articles, subcutaneous implants or intramuscular devices of cylinderical , bullet, elliptical, circular, disk or other shape that is appropriate for placement in the physiological environments.

Other articles made according to the invention include implants, prostheses or artificial glands for dispensing a water-soluble bioactive factor to a local cell population. In this embodiment, the polymer matrix acts as a support for the surrounding bone, or cartilage tissue.

The composition of the present invention can be formulated for delivering a soluble, bioactive factor to a local cell population to produce the desired localized effect. The composition can be used in animals, including warm-blooded animals, humans, primates, farm and sport animals, laboratory animals, reptiles and amphibians. The amount of bioactive factor is, in one embodiment, the amount necessary to affect the local cell population, or an excess of that amount. Generally, the article can contain from about 5 mg to about 30 mg of protein. The articles made from the composition of the present invention can be manufactured by standard techniques, such as casting or compression molding. Other methods of shaping polymeric materials into articles having the desired size and shape are well known. In one embodiment of the present invention, the dried polymer is blended with the protein in the desired proportion, and the mixture is pressed into circular disks by compression molding. Compression- molded articles can then be further sectioned into pieces having the desired dimensions.

Polyanhydrides have demonstrated the character- istics necessary for a successful delivery vehicle of osteogenic factors. They released the

inductive protein(s) at an effective dose over a time period coincident with the accumulation of host target cells , as evidenced by the appearance of cartilage and/or bone at the ectopic site. In addition, there was rapid ingrowth of host tissue to promote direct interaction of bioactive factors with the target cells. The polymers are biocompatible , and the composition is biodegradable so that it will ultimately be resorbed. It should be emphasized that the water-soluble proteins for use in the present invention although capable of inducing a biological effect iH_y_L_t__r do not induce an effect when implanted alone into the physiological site. Similiarly, the polymers themselves do not induce an effect when implanted alone. Only the combination of water-soluble proteins and polymer was effective.

Polyanhydride polymers have now been shown capable of delivering bioactive factors which act on local cell populations. In addition to chondro/osteogenic factors, bioactive factors such as TGF-beta, EGF, FGF, and PDGF which act upon local cell populations in would healing or angiogenesis , can be used in the present devices. The invention is further illustrated by the following exemplification.

EXEMPLIFICATION

MATERIALS AND METHODS

_ζ£Eiϊϊ_-_-i£2_£-!_ϊ_-.!; -£. £-ky£i^ matri-x Water-soluble proteins were prepared from a 4 M guanidine hydrochloride extract of demineralized bovine cortical bone as described by Syftestad et al. Syftestad et al., Differentiation, 2?:230-237 (1985). Briefly, mid-shaft femoral cortices of 1 year old steers were cleaned of adhering tissue and marrow, decalcified in 0.6 N HC1 at 4°C, defatted in chloroform:methanol (1:1 v/v) and air dried. The bone matrix was extracted at 4°C in a solution of 4 M guanidine hydrochloride buffered with 50 mM Tris , pH 6.8, and containing enzyme inhibitors. The extract was dialyzed at 4 ^β C sequentially against solutions of decreasing ionic strength: 0.5 M guanidine hydrochloride, 50 mM Tris buffered saline, and distilled water. Precipitates which formed at each step were removed by centrifugation until only those proteins soluble in cold distilled water remained. This portion of the extract was lyophrlized and will hereafter be referred to as water-soluble proteins.

rep ration of polyanhydride polymers

Poly[bis(p-carboxyphenoxy)propane anhydride] (PCPP) and poly[bis (p-carboxy)methane anhydride] (PCPM) were synthesized by melt polycondensation.

Conix, Macr£_ _; ___3ynth_^, 2:95-98 (1966); Leong et al . , l_._Bi£IS£_-___Mat____Res___, l£:941-955 (1985). Briefly, the dicarboxylic acid monomers were converted to the mixed anhydride by total reflux in acetic anhydride followed by recrystallization. The prepolymers were then subjected to melt polycondensation in vacuo under nitrogen sweep. Copolymers of PCPP and sebacic acid (SA) were obtained in a similar manner. The polymers were purified by extraction with anhydrous ether in a Soxhlet Extractor for several hours and were stored in a desicator over calcium chloride .

Matrices incorporating water-soluble protein were formulated by compression molding. The poly- mers were ground in a Micro Mill Grinder and sieved into a particle size range of 90-150 μm . Twenty mg of water-soluble proteins were manually mixed with the polymer at the desired ratios (w/w) and the mixture pressed into circular discs in a Carver Test Cylinder Outfit at 30 Kpsi and room temperature.

The dimensions of the devices were 14 mm in diameter and 0.9 to 1.1 mm thick. They were manually sec-

3 tioned into 1 mm disks immediately prior to im¬ plantation.

iS_∑iy.£_i_ ^s . ^s .£Y.

Under Metophane anaesthesia, a 1 cm incision was made in the dorsal thigh of 5-7 week old CBA/J mice. The implants were placed between muscle beds, care being taken to avoid contact with the femur. The wound was sealed by clips and swabbed with

alcohol. The animals were monitored for signs of inflammation or obvious discomfort, at which time the animal was euthanized and the implant discarded. NIH guidelines for the care and use of laboratory animals (NIH Publication #85-23 Rev. 1985) were observed. The healthy samples were removed 9 or 16 days post-implantation fixed in Perfix (Fisher Scientific), decalcified (if necessary), and processed for histology. Alternate paraffin- embedded sections 5-6 μm thick were stained with either Toluidine blue or Mallory-Heidenhain' s stain.

Cartilage was identified by its typical morphology of round cells embedded in an extensive extracellular matrix and by the characteristic metachromatic staining of the extracellular matrix with Toluidine blue. Bone was identified by its characteristic morphology of lining osteoblasts, multinucleated osteoclasts, and osteocytes embedded osteoid and by the dark blue staining of the osteoid with Mallory-Heidenhain' s ^" stain. No attempt was made to quantitate the amount of cartilage and/or bone present.

RESULTS

The water-soluble protein preparation from bovine bone matrix used in this study has been previously shown to consist of numerous Coomassie Blue stained protein bands ranging in size from 10 Kd to 100 Kd when subjected to SDS-PAGE. Syftestad et al. , Differentiation, 29:230-237 (1985). The water-soluble proteins are capable of inducing

chondrogenesis in two i_n_yi^tr£ assay systems: the stage 24 chick limb bud system (Syftestad and Caplan, Dev____Bi£______, 104:348-356 (1984); Syftestad et ^al - _> Differentiation, 29:230-237 (1985)), and day 11 chich embryonic minced muscle explants. Lucas et ^a1 - ' Pill£££Sti ^a _.i£H. 37:47-52 (1987). When properly formatted in a controlled-release device of the present invention, this protein mixture can also induce ectopic endochondral ossification in the muscle of CBA/J mice. When 20 mg of lyophilized water-soluble proteins were implanted alone into a mouse thigh muscle, however, no signs of cartilage or bone formulation could be detected. Nine days after implantation a "nodule" of connective tissue composed of fibroblastic cell types embedded in a loose extracellular matrix was present. This response is most probably due to the normal wound healing response and was not directly initiated by the implanted water-soluble proteins. By 16 days post-implantation, this connective tissue infiltrate has disappeared making it impossible to locate the original implant site.

Implantation of the polymers, PCPP-SA co- polymer, PCPP, or PCPM, alone without the addition of water-soluble proteins also resulted in the accumulation of connective tissue composed of fibroblastic cells as described above. At 9 days post- implantation, polymer and connective tissue cells were visible for PCPP, and PCPP-SA. The connective tissue was unchanged at 16 days post- implantation. None of the polymer implants alone exhibited any formation of cartilage and/or bone (Table 1) .

TABLE 1

Number of Implants Amount of with Cartilage or Bone/

__£____£.__ . H_.£ ^r -_-i£-LH£-L _P_.£_.£iϊl !-HE£ ^r ._£ _i_5E-k-_-_£i-. Water-soluble 20 mg 0/8 proteins

PCPP-SA 30:70 0 mg 0/6

PCPP-SA 30:70 20% loading 20 mg 0/4 30% loading 20 mg 0/4 40% loading 20 mg 0/4

PCPP 0 mg 0/6

PCPP

20% loading 20 mg 0/4 40% loading 20 mg 0/4

60% loading 20 mg 3/10

PCPM 0 mg 0/6

PCPM

20% loading 20 mg 0/4 ³ 0% loading 20 mg 6/12

40% loading 20 mg 0/4

50% loading 20 mg 0/4

When water-soluble proteins were incorporated into PCPP-SA copolymers (ratio of PCPP:SA was 30:70) with 20% loading of protein, the result was the accumulation of connective tissue and inflammatory cells 9 days pos -implantatio . There was no observable cartilage and/or bone in any of the implants (Table 1) . Increasing the loading of protein to 30 and 40% did not result in the induc¬ tion of cartilage and/or bone (Table 1). PCPP was tested at protein loadings of 20% and 40%. At these loadings, the implants exhibited connective tissue 9 days post-implantation and were essentially indistinguishable from controls. No cartilage and/or bone was induced (Table 1). However, when the loading was increased to 60%, cartilage was observed at 9 days post-implantation and bone at 16 days post-implantation. The induced cartilage and bone was formed adjacent to the pieces of polymer. The incidence of osteogenesis in the implants was 30%.

PCPM was tested at a variety of loading with water-soluble proteins: 20, 30, 40 and 50%. Only the implants loaded with 30% protein exhibited cartilage and/or bone induction (Table 1). The others contained connective tissue and were es¬ sentially identical to implants of PCPM alone. However, at 40% loading, cartilage was observed at day 9 post-implantation. The nodules of cartilage were being invaded by vaculature and the beginning of osteogenesis was observable. The nodules of cartilage and bone were usually formed adjacent to

the particles of polymer, but occasionally small particles of polymer could be discerned within the nodule of cartilage. By 16 days post- implantation the cartilage had been replaced by a nodule of trabecular bone. The incidence of induction of cartilage and/or bone in the implants was 50% (Table 1).

..;£Hi_-_.i£Σ--

Those skilled in the art will recognize, or be able to ascertain using no more than routine experi¬ mentation, many equivalents to the specific embodi¬ ments of the invention described herein. Such equivalents are intended to be encompassed by the following claims.