PURPOSE: To prevent the chipping and dislodgment of a tip and to improve the service life thereof by executing brazing by using a Cu alloy made of a compsn. contg. specific ratios of Zn, Mn, and Co and consisting of the balance Cu and unavoidable impurities.
CONSTITUTION: A sintered hard alloy member and steel member are brazed by using the Cu alloy contg. 35W45% Zn, 1.5W3% Mn, and 1.5W3% Co. The brazing is executed at 0.25W0.5mm brazing allowance and ≤975°C brazing temp. The brazed members are preferably cooled at ≥5°C/sec cooling rate until the brazing filler metal solidifies after the completion of brazing. The uniform structure is thereby formed and as a result, the brazing layer which has low high-temp. deformation resistance, small residual stress after the brazing, and high ordinary-temp. strength is obtd.
YOSHIDA HIDEAKI